1.2550 60WCrV7 |
 |
|
 |
1.2550 60WCrV7 is a high duty shock resisting alloy tool steel. In the hardened condition 1.2550 60WCrV7 is a heat resisting tool steel that combines great hardness with good toughness and shock resisting properties. |
TYPICAL ANALYSIS |
|
|
|
|
C. |
Si. |
Mn. |
Cr. |
V. |
0.50% |
0.80% |
1.50% |
2.50% |
0.20% |
Forging:
Heat the 1.2550 tool steel component slowly and uniformly to 1000°C. Forge within a range of 1000/800°C, reheating if necessary. Cool slowly (preferably in a furnace) to avoid setting up stresses.
Annealing:Heat the 1.2550 tool uniformly to 770°C, equalise, then furnace cool.
Stress Relieving:If machining operations have been heavy or if the 1.2550 tool has an unbalanced section, remove stresses before hardening by heating up to 700°C, equalise, then cool slowly.
Hardening:Pre heat the 1.2550 tool steel to 650°C and thoroughly soak. Continue heating to the final hardening temperature of 900/950°C. Allow sufficient time for the component to be heated through. Quench in oil.
Martempering:Martempering is an alternative hardening procedure for 1.2550 which may be used when suitable salt bath equipment is available.
Tempering:Heat uniformly and thoroughly at the selected tempering temperature and hold for at least one hour per inch of total thickness.
| Tempering °C |
150 |
200 |
250 |
350 |
400 |
HRc |
62/61 |
61/60 |
60/59 |
58/57 |
55/54 |
|